Experimental data for shear viscosity vs. shear rate are as follows:
visco_200.crv
(viscosity vs. shear rate at 200° C):1.0476158e-01 4.7409219e+04 1.5199111e-01 4.4989727e+04 2.2051308e-01 4.2269406e+04 3.1992671e-01 3.8987227e+04 4.6415886e-01 3.5058137e+04 6.7341506e-01 3.0742695e+04 9.7700995e-01 2.6492119e+04 1.4174742e+00 2.2641396e+04 2.0565124e+00 1.9267033e+04 2.9836473e+00 1.6254397e+04 4.3287611e+00 1.3465704e+04 6.2802911e+00 1.0877272e+04 9.1116276e+00 8.5747520e+03 1.3219412e+01 6.6494995e+03 1.9179104e+01 5.1295151e+03 2.7825592e+01 3.9814446e+03 4.0370174e+01 3.1410603e+03 5.8570202e+01 2.5388992e+03 8.4975342e+01 2.1135415e+03
visco_220.crv
(viscosity vs. shear rate at 220° C):1.0476158e-01 3.2600383e+04 1.5199111e-01 3.1115115e+04 2.2051308e-01 2.9555596e+04 3.1992671e-01 2.7824447e+04 4.6415886e-01 2.5750273e+04 6.7341506e-01 2.3249219e+04 9.7700995e-01 2.0457902e+04 1.4174742e+00 1.7664730e+04 2.0565124e+00 1.5109322e+04 2.9836473e+00 1.2866907e+04 4.3287611e+00 1.0875361e+04 6.2802911e+00 9.0399053e+03 9.1116276e+00 7.3314004e+03 1.3219412e+01 5.7986880e+03 1.9179104e+01 4.5048770e+03 2.7825592e+01 3.4752805e+03 4.0370174e+01 2.6930635e+03 5.8570202e+01 2.1181692e+03 8.4975342e+01 1.7051194e+03
visco_240.crv
(viscosity vs. shear rate at 240° C):1.0476158e-01 2.2935412e+04 1.5199111e-01 2.2018766e+04 2.2051308e-01 2.1021365e+04 3.1992671e-01 1.9975033e+04 4.6415886e-01 1.8819420e+04 6.7341506e-01 1.7439488e+04 9.7700995e-01 1.5771608e+04 1.4174742e+00 1.3898310e+04 2.0565124e+00 1.2011361e+04 2.9836473e+00 1.0277535e+04 4.3287611e+00 8.7546172e+03 6.2802911e+00 7.4047461e+03 9.1116276e+00 6.1631475e+03 1.3219412e+01 5.0064775e+03 1.9179104e+01 3.9653857e+03 2.7825592e+01 3.0831277e+03 4.0370174e+01 2.3787000e+03 5.8570202e+01 1.8422029e+03 8.4975342e+01 1.4472250e+03
Experimental data for the storage and loss moduli ( and ) are as follows:
gprime.crv
( vs. angular frequency curve at 220° C):0.1 593.16 0.1585 1178.4 0.2512 2207.6 0.3981 3917.3 0.631 6559.3 1 10419 1.585 15724 2.512 22596 3.9813 31232 6.3101 41570 10.001 53470 15.85 66881 25.121 81509 39.813 97119 63.101 113520 100 130360
gsecond.crv
( vs. angular frequency curve at 220° C):0.1 3215.8 0.1585 4782 0.2512 6932.5 0.3981 9740.3 0.631 13239 1 17346 1.585 22001 2.512 27050 3.9813 32279 6.3101 37352 10.001 42321 15.85 46851 25.121 51123 39.813 55108 63.101 59097 100 63270
The files for these data curves are provided on the Ansys Polyflow product CD, in the test/polymat/example3 subdirectory.